AISI 1080 is a plain carbon steel containing nominally 0.80% carbon; it has relatively low hardenability. It may be used in the as-rolled, annealed, normalized or liquid-quenched-and-tempered condition, depending on the required properties.
1080 Forging Steel is an excellent steel for beginning knife makers and professionals alike. An ideal choice for forging and for layering with 15N20 for Damascus. Hot rolled and annealed. Requires less soak time in heat before quenching and is very forgiving during the heat treat process making it great for heat treating in a forge.
| Composition |
|
| Mechanical Properties |
| Properties | Conditions | ||
| T (°C) | Treatment | ||
| Density (×1000 kg/m3) | 7.7-8.03 | 25 | |
| Poisson's Ratio | 0.27-0.30 | 25 | |
| Elastic Modulus (GPa) | 190-210 | 25 | |
| Tensile Strength (Mpa) | 615.4 | 25 | annealed at 790°C more |
| Yield Strength (Mpa) | 375.8 | ||
| Elongation (%) | 24.7 | ||
| Reduction in Area (%) | 45.0 | ||
| Hardness (HB) | 174 | 25 | annealed at 790°C more |
| Impact Strength (J) (Izod) | 6.1 | 25 | annealed at 790°C more |
| Thermal Properties |
| Properties | Conditions | ||
| T (°C) | Treatment | ||
| Thermal Expansion (10-6/ºC) | 14.7 | 20-700 more | annealed |
| Thermal Conductivity (W/m-K) | 48.1 | 100 more | |
| Specific Heat (J/kg-K) | 490 | 50-100 more | |
We are happy to answer any questions you have regarding our product lines and services. Please tell us a little more about yourself and we will have someone contact you as soon as possible.
Speak to a Steel Expert
| carbon steel tread plate | 1010 carbon steel plate |
| 1 4 carbon steel plate | 1015 carbon steel plate |
| 1 8 carbon steel plate | 1018 carbon steel plate |
| 1/2 carbon steel plate | 1020 carbon steel 1 8 plate |
| 1/4 inch carbon steel plate | 1020 carbon steel plate |
| 1095 carbon steel plate | 1025 carbon steel plate |
| 3 16 carbon steel plate | 1030 carbon steel plate |
| 3 8 carbon steel plate | 1035 carbon steel plate |
WeChat
home